HOME > Introduction of Grades

Introduction of Grades

Feature Solid Liquid Solid Liquid
High crystallinity Softness Low viscosity Abrasion resistance Chemical resistance Abrasion resistance Chemical resistance Abrasion resistance
Grade T6002 T6001 T5652 T5651 T5650J T5650E G4672 T4671 T4692 T4691 G3452 G3450J
Molecular weight
(Mn)
2,000 1,000 2,000 1,000 800 500 2,000 1,000 2,000 1,000 2,000 800
Appearence White solid White solid Viscous liquid Viscous liquid Viscous liquid Viscous liquid Viscous liquid*) Viscous liquid*) White solid White solid Viscous liquid Viscous liquid
OH Value
(mgKOH/g)
51
~ 61
100
~ 120
51
~ 61
100
~ 120
130
~ 150
200
~ 250
46
~ 56
100~
120
51
~ 61
100
~ 120
51
~ 61
130
~ 150
Viscosity
mPa • s(at 50°C)
6,000
~15,000
1,100
~2,300
7,000
~16,000
1,200
~2,400
600
~1,200
200
~430
12,000
~2,500
1,500
~3,000
3,000*2
~8,000
500*2
~1,500
6,800*2
~13,000
400*2
~800
Malting point
(°C)
40~50 ≦-5 5~15 50~60 ≦-5
UN Class Not applicable Not applicable Not applicable Not applicable Not applicable
*1 Partial crystallization may arise occasionally.  *2 The value at 70°C



Cf)mPa•s=Pa•s×10-3=1cP
The data shown are typical values and should not be used as apecifications.
Mn:Number avarage Molecular weight

ZoomZoom

Feature Solid Liquid Solid Liquid
High crystallinity Softness Low viscosity Abrasion resistance Chemical resistance Abrasion resistance Chemical resistance Abrasion resistance
Grade T6002 T6001 T5652 T5651 T5650J T5650E G4672 T4671 T4692 T4691 G3452 G3450J
Molecular weight
(Mn)
2,000 1,000 2,000 1,000 800 500 2,000 1,000 2,000 1,000 2,000 800
Appearence White solid White solid Viscous liquid Viscous liquid Viscous liquid Viscous liquid Viscous liquid*) Viscous liquid*) White solid White solid Viscous liquid Viscous liquid
OH Value
(mgKOH/g)
51
~ 61
100
~ 120
51
~ 61
100
~ 120
130
~ 150
200
~ 250
46
~ 56
100~
120
51
~ 61
100
~ 120
51
~ 61
130
~ 150
Viscosity
mPa • s(at 50°C)
6,000
~15,000
1,100
~2,300
7,000
~16,000
1,200
~2,400
600
~1,200
200
~430
12,000
~2,500
1,500
~3,000
3,000*2
~8,000
500*2
~1,500
6,800*2
~13,000
400*2
~800
Malting point
(°C)
40~50 ≦-5 5~15 50~60 ≦-5
UN Class Not applicable Not applicable Not applicable Not applicable Not applicable
*1 Partial crystallization may arise occasionally.  *2 The value at 70°C



Cf)mPa•s=Pa•s×10-3=1cP
The data shown are typical values and should not be used as apecifications.
Mn:Number avarage Molecular weight