Physical Properties
Lithium-ion Battery Separator
| Physical properties | Test method | BH500 | UH650 | |
|---|---|---|---|---|
| Average molecular weight (Mv) | 106g/mol | Asahi Kasei method | 0.5 | 0.9 |
| Bulk density | g/cm3 | Asahi Kasei method | 0.5 | 0.5 |
| Density | g/cm3 | ISO 1183-2 | 0.94 | 0.94 |
| Average particle size | μm | JIS K0069 | 100 | 110 |
| Melting point | ℃ | JIS K 7121 | 136 | 136 |
Lead Acid Battery Separator
| Physical properties | Test method | UH910 | UH950 | |
|---|---|---|---|---|
| Average molecular weight (Mv) | 106g/mol | Asahi Kasei method | 3 | 4 |
| Bulk density | g/cm3 | Asahi Kasei method | 0.5 | 0.5 |
| Density | g/cm3 | ISO 1183-2 | 0.93 | 0.93 |
| Average particle size | μm | JIS K0069 | 100 | 110 |
| Melting point | ℃ | JIS K 7121 | 136 | 137 |
High-strength Fiber
| Physical properties | Test method | UH901 | UH951 | |
|---|---|---|---|---|
| Average molecular weight (Mv) | 106g/mol | Asahi Kasei method | 3 | 4 |
| Bulk density | g/cm3 | Asahi Kasei method | 0.5 | 0.5 |
| Density | g/cm3 | ISO 1183-2 | 0.93 | 0.93 |
| Average particle size | μm | JIS K0069 | 100 | 110 |
| Melting point | ℃ | JIS K 7121 | 136 | 137 |
Molding
| Physical properties | Test method | UH910 | UH950 | UH972 | |
|---|---|---|---|---|---|
| Average molecular weight (Mv) | 106g/mol | Asahi Kasei method | 3 | 4 | 6 |
| Bulk density | g/cm3 | Asahi Kasei method | 0.5 | 0.5 | 0.5 |
| Density | g/cm3 | ISO 1183-2 | 0.93 | 0.93 | 0.92 |
| Average particle size | μm | JIS K0069 | 100 | 110 | 80 |
| Melting point | ℃ | JIS K 7121 | 136 | 137 | 134 |