Typical Properties
MKS system of units
m-PPE solid | ||||||
---|---|---|---|---|---|---|
Expand ratio | 【cc/g】 | 5 | 7 | - | ||
Bulk Density | ASTM D792 | 【pcf】 | 12.5 | 8.7 | 67 | |
g/L | 200 | 140 | 1080 | |||
Tensile stress | ISO1798 ASTN D412 (JIS K6767) |
strength | 【psi】 | 377 | 261 | |
elongation | 【%】 | 2 | 2 | |||
Compressive stress | ISO 844 (JIS K7220) |
5% | 【psi】 | 334 | 232 | |
10% | 【psi】 | 421 | 276 | |||
Tear strength | ASTM D624 (JIS K6767) |
【N/cm】 | 100 | 66.2 | ||
Hardness | JIS K6253 | Duromater | E93 | E89 | ||
Flexural | ISO 1209 (JIS K7221) |
strength | 【psi】 | 667 | 392 | |
strain | 【%】 | 3.8 | 3.4 | |||
Friction resistance | ASTM D1044 | 60rpm-1000r 8.8ozg |
【oz】 | 0.21 | 0.21 | 0.12 |
Flammability | UL94 | 3mm=0.118" | V-0 | V-0 | V-0 | |
5mm=0.197" | V-0 | V-0 | V-0 | |||
Oxygen index | ISO 4589 (JIS K7201) | 【%】 | 29 | 29 | 29 | |
Shrinkage | JIS K6767 | 100℃=212degF | 【%】 | 0.6 | 0.8 | |
Coefficient of linear expansion |
ASTM D969 | 5~40℃ 41~104degF |
【mm/mm・℃】 | 5×10-5 | 7×10-5 | |
Thermal conductivity |
ISO 8302 (JIS A1412) |
【W/m・K】 | 0.041 | 0.038 | 0.15 | |
Fogging | IEC 6452 | 100℃x 3hrs 212degF x 3hrs |
Gloss【%】 | 99.0 | 99.3 | |
Haze【%】 | 0.2 | 0.2 | ||||
Breakdown voltage | IEC 60243 | 【kV/mm】 | 5.1 | 4.6 | 29 |
SI system of units
m-PPE solid | ||||||
---|---|---|---|---|---|---|
Expand ratio | 【cc/g】 | 5 | 7 | - | ||
Bulk Density | ASTM D792 | g/L | 200 | 140 | 1080 | |
Tensile stress | ISO1798 ASTN D412 (JIS K6767) |
strength | 【Mpa】 | 2.6 | 1.8 | |
elongation | 【%】 | 2 | 2 | |||
Compressive stress | ISO 844 (JIS K7220) |
5% | 【Mpa】 | 2.3 | 1.6 | |
10% | 【Mpa】 | 2.9 | 1.9 | |||
Tear strength | ASTM D624 (JIS K6767) |
【N/cm】 | 100 | 66.2 | ||
Hardness | JIS K6253 | Duromater | E93 | E89 | ||
Flexural | ISO 1209 (JIS K7221) |
strength | 【Mpa】 | 4.6 | 2.7 | |
strain | 【%】 | 3.8 | 3.4 | |||
Friction resistance | ASTM D1044 | 60rpm-1000r 250g |
【mg】 | 6 | 6 | 3.4 |
Flammability | UL94 | 3mm | V-0 | V-0 | V-0 | |
5mm | V-0 | V-0 | V-0 | |||
Oxygen index | ISO 4589 (JIS K7201) | 【%】 | 29 | 29 | 29 | |
Shrinkage | JIS K6767 | 100℃ | 【%】 | 0.6 | 0.8 | |
Coefficient of linear expansion |
ASTM D969 | 5~40℃ | 【mm/mm・℃】 | 5×10-5 | 7×10-5 | |
Thermal conductivity |
ISO 8302 (JIS A1412) |
【W/m・K】 | 0.041 | 0.038 | 0.15 | |
Fogging | ISO 6452 | 100℃ 3hrs | Gloss【%】 | 99.0 | 99.3 | |
Haze【%】 | 0.2 | 0.2 | ||||
Breakdown voltage | IEC 60243 | 【kV/mm】 | 5.1 | 4.6 | 29 |